Properties of ZrN films as substrate masks in liquid phase epitaxial lateral overgrowth of compound semiconductors
D. Dobosz, K. Golaszewska*, Z. R. Zytkiewicz, E. Kaminska*, A. Piotrowska*, T. T. Piotrowski*, A. Barcz, and R. Jakiela
Institute of Physics, Polish Academy of Sciences, Al. Lotnikow 32/46, 02-668 Warszawa, Poland
*Institute of Electron Technology, Al. Lotnikow 32/46, 02-668 Warszawa, Poland
| Keywords | epitaxial lateral overgrowth, selective epitaxy, liquid phase epitaxy |
| PACS | 81.05.Ea, 81.15.Lm, 68.35.Gy, 68.55.Jk, 73.40.Ns, 73.61.At |
| DOI | 10.1002/crat.200410373 |
The usefulness of ZrN films as masks for epitaxial lateral overgrowth of GaAs and GaSb by liquid phase epitaxy is studied. It was observed that during the growth process ZrN masks are mechanically stable, they adhere strongly to the substrate and do not show any signs of degradation even at the growth temperature as high as 750°C. Moreover, perfect selectivity of GaAs and GaSb epitaxy was obtained on ZrN masked substrates ensuring the growth wide and thin layers. To study the influence of growth conditions on electrical resistivity of the mask, ZrN films deposited on GaAs substrates were annealed in various atmospheres. It was found that at temperatures higher than about 580°C the ZrN masks become highly resistive when heat-treated in hydrogen flow employed during growth. Usually, LPE growth temperature for GaAs is higher. Thus, ELO growth of GaAs by LPE becomes more difficult, though still possible, if ZrN masks are to be applied as buried electrical contacts. For GaSb ELO layers however, typical LPE growth temperature is about 480°C. This allows us to grow high quality GaSb ELO layers by LPE still preserving high electrical conductivity of ZrN mask.